Waterborne polymer series for architectural decoration coatings
| Product name | Performance indicators | applications | performance | |
| HN-101 | Appearance | light blue liquid | Interior wall paint, color tile paint & etc | Styrene-acrylic emulsion, has excellent scrubbing and water resistance. |
| Solid content | 47±2wt% | |||
| Viscosity.cps(25℃) | 1000-4000cps | |||
| PH | 7.0-8.0 | |||
| Glass Transition Temperature (Tg) | 26℃ | |||
| Minimum Film Formation Temperature（MFT） | 22-24℃ | |||
| Ca2+ stability 5%CaCl2: emulsion =1:3, 48h, No Flocculation, No Stratification. | Pass | |||
| HN-102 | Appearance | light blue liquid | internal and external general paint | Styrene-acrylic emulsion, has excellent scrubbing resistance, water and alkali resistance, and good shear stability. |
| Solid content | 48±1wt% | |||
| Viscosity.cps(25℃) | 500-3000 | |||
| PH | 7.0-8.0 | |||
| Glass Transition Temperature (Tg) | 24℃ | |||
| Minimum Film Formation Temperature（MFT） | 21-23℃ | |||
| Ca2+ stability 5%CaCl2: emulsion =1:3, 48h, No Flocculation, No Stratification. | Pass | |||
| HN-996 | Appearance | light blue liquid | General internal and external paint | Styrene-acrylic emulsion, has excellent scrubbing resistance, water and alkali resistance, color spreading, good shear stability and high gloss. |
| Solid content | 49±1wt% | |||
| Viscosity.cps(25℃) | 500-3000 | |||
| PH | 7.0-8.0 | |||
| Glass Transition Temperature (Tg) | 22℃ | |||
| Minimum Film Formation Temperature（MFT） | 18-20℃ | |||
| Ca2+ stability 5%CaCl2: emulsion =1:3, 48h, No Flocculation, No Stratification. | Pass | |||
| HN-01F | Appearance | light blue liquid | As a general purpose primer for the internal and external walls | The acrylate emulsion has excellent wet adhesion, permeability and alkali resistance. |
| Solid content | 29±1wt% | |||
| Viscosity.cps(25℃) | ≤500cps | |||
| PH | 7.5-8.5 | |||
| Minimum Film Formation Temperature（MFT） | 10℃ | |||
| HN-314T | Appearance | light blue liquid | Elastic putty, elastic paint, the external wall insulation system, etc | Elastic styrene-acrylic emulsion, prepared by functional crosslinking monomers, has excellent elongation, outstanding sexual resistant and adhesion. |
| Solid content | 48±1wt% | |||
| Viscosity.cps(25℃) | 1000-3000 | |||
| PH | 7.0-8.0 | |||
| Glass Transition Temperature (Tg) | -15℃ | |||
| Minimum Film Formation Temperature（MFT） | 0℃ | |||
| Ca2+ stability 5%CaCl2: emulsion =1:3, 48h, No Flocculation, No Stratification. | Pass | |||
| HN-519NT | Appearance | light blue liquid | Elastic putty, elastic paint, the external wall insulation system, etc | Self-crosslinking acrylic elastic emulsion, excellent tensile, elastic and elongation, outstanding sexual resistant and adhesion. |
| Solid content | 48±1wt% | |||
| Viscosity.cps(25℃) | 100-1000 | |||
| PH | 7.0-8.0 | |||
| Glass Transition Temperature (Tg) | -40℃ | |||
| Minimum Film Formation Temperature（MFT） | 0℃ | |||
| Ca2+ stability 5%CaCl2: emulsion =1:3, 48h, No Flocculation, No Stratification. | Pass | |||
| Product name | Performance indicators | applications | performance | |
| HN-9105A | Appearance | light blue liquid | decorative textured wall coatings | Silicone modified styrene-acrylic emulsion, core-shell structure, high water resistance, anti-whiteness, strong adhesion, good adhesion, fast drying, good film formation, excellent early water resistance. |
| Solid content | 44±1wt% | |||
| Viscosity.cps(25℃) | 2000-8000 | |||
| PH | 7.0-8.0 | |||
| Minimum Film Formation Temperature（MFT） | 21-22℃ | |||
| Product name | Performance indicators | applications | performance | |
| HN-9301C | Appearance | light blue liquid | Continuous phase of multicolored paint | Good permeability, does not affect spray、dry color presentation |
| Solid content | 37±1wt% | |||
| Viscosity.cps(25℃) | ＜100 | |||
| Particle Size（nm） | 60-70 | |||
| PH | 7.0-8.0 | |||
| Minimum Film Formation Temperature（MFT） | 8℃ | |||
| Ca2+ stability 5%CaCl2: emulsion =1:3, 48h, No Flocculation, No Stratification. | Pass | |||
| HN-9311S | Appearance | light blue liquid | Disperse phase of colorful coating | Package, impermeable color performance, water resistance, excellent adhesion. |
| Solid content | 47±1wt% | |||
| Viscosity.cps(25℃) | 100-2000 | |||
| Particle Size（nm） | 90-120 | |||
| PH | 7.0-8.0 | |||
| Minimum Film Formation Temperature（MFT） | 29℃ | |||
| Ca2+ stability 5%CaCl2: emulsion =1:3, 48h, No Flocculation, No Stratification. | Pass | |||
Waterborne adhesive
| Product name | Performance indicators | applications | performance | |
| HN-SL530 | Appearance | light blue | Mainly used for wet curtain bonding and other industrial adhesives for refrigeration systems | Self-crosslinking styrene-acrylic emulsion, has strong adhesion, good water resistance, long service time, free from heavy metals, and has stable mechanical and physical properties, not prone to deterioration, easy to store. |
| Solid content | 34±1wt% | |||
| Viscosity.cps(25℃) | 2500-4000 | |||
| PH | 4.0-6.0 | |||
| Minimum Film Formation Temperature（MFT） | 0℃ | |||
| Product name | Performance indicators | applications | performance | |
| HN-2018S | Appearance | light blue | Used for flexible adhesive of glass fiber mesh fabric, best compatible with the production Gk-3451HF | This product is self-crosslinking emulsion with high cohesive strength, firm positioning, high elasticity and good alkali resistance. |
| Solid content | 34±1wt% | |||
| Viscosity.cps(25℃) | ≤150 | |||
| PH | 6.0-7.0 | |||
| Minimum Film Formation Temperatu（MFT） | 0℃ | |||
| HN-3451HF | Appearance | Milky white slightly blue | Used for hard adhesive of glass fiber grid cloth, best compatible with the production Gk-2018S | This product is self-crosslinking emulsion, high adhesion with glass fiber, good alkali resistance, high gloss, non-moisture back adhesion. |
| Solid content | 34±1wt% | |||
| Viscosity.cps(25℃) | ≤150 | |||
| PH | 6.0-7.0 | |||
| Minimum Film Formation Temperature（MFT） | 45℃ | |||
| Product name | Performance indicators | applications | performance | |
| HN-122 | Appearance | milk white liquid | Water-based laminating adhesives. | Less adhesive consumption, high adhesion. |
| Solid content | 48±1wt% | |||
| Viscosity.cps(25℃) | 8000-30000 | |||
| PH | 7.5-8.5 | |||
| Glass Transition Temperature (Tg) | -27℃ | |||
| Minimum Film Formation Temperature（MFT） | 0℃ | |||
| Product name | Performance indicators | applications | performance | |
| HN-9827 | Appearance | Translucency and light blue liquid | Sponge adhesive | Play a hard effect, stretching on the glue set does not rebound. |
| Solid content | 39±1wt% | |||
| Viscosity.cps(25℃) | 3000-5000 | |||
| Particle Size（nm） | 60-100 | |||
| PH | 6.0-8.0 | |||
| Product name | Product indicators | applications | performance | ||
| HN-6019 | Appearance | ||||
| Solid content | 50±1wt% | 50±1wt% | |||
| Viscosity.cps(25℃) | |||||
| Particle Size（nm） | |||||
| PH | 7-9 | 7-9 | |||
Waterborne polymer series for building sealant
| Product name | Performance indicators | applications | performance | |
| HN-154VE | Appearance | milk white liquid | Sealant adhesive for construction, ceramic tile adhesive, etc | Vinyl acetate-acrylate copolymer, has good stability and water resistance, has high bearing capacity to powder and good adhesion. |
| Solid content | 53±1wt% | |||
| Viscosity.cps(25℃) | 100-500 | |||
| PH | 3.5-4.5 | |||
| Glass Transition Temperature (Tg) | -18℃ | |||
| Minimum Film Formation Temperature（MFT） | 0℃ | |||
| Product name | Performance indicators | applications | performance | |
| HN-1025 | Appearance | light blue | Water-proof sealant for construction, ceramic tile adhesive, etc | Elastic styrene-acrylic emulsion, has good stability and water resistance, has high bearing capacity to powder and good adhesion. |
| Solid content | 47±1wt% | |||
| Viscosity.cps(25℃) | 1000-5000 | |||
| PH | 7.0-8.0 | |||
| Minimum Film Formation Temperature（MFT） | 16-18℃ | |||
| Ca2+ stability 5%CaCl2: emulsion =1:3, 48h, No Flocculation, No Stratification. | pass | |||
| Product name | Performance indicators | applications | performance | |
| HN-166T | Appearance | light blue | High elastic silicone sealant | Silicone modified acrylate emulsion, has good weather resistance quick curing, stability, water resistance, toughness, resilience and good adhesion. |
| Solid content | 50±1wt% | |||
| Viscosity.cps(25℃) | 1500-3000 | |||
| PH | 6.0-7.0 | |||
| Minimum Film Formation Temperature（MFT） | 0℃ | |||
| Ca2+ stability 5%CaCl2: emulsion =1:3, 48h, No Flocculation, No Stratification. | pass | |||
| HN-167T | Appearance | light blue | High elastic silicone sealant | Silicone modified acrylate emulsion, has good weather resistance quick curing, stability, water resistance, toughness, resilience and good adhesion. |
| Solid content | 50±1wt% | |||
| Viscosity.cps(25℃) | 5000-8000 | |||
| PH | 6.0-7.0 | |||
| Minimum Film Formation Temperature（MFT） | 0℃ | |||
| Ca2+ stability 5%CaCl2: emulsion =1:3, 48h, No Flocculation, No Stratification. | pass | |||
| Product name | Performance indicators | applications | performance | |
| HN-168T | Appearance | light blue | High elastic silicone sealant | Silicone modified acrylate emulsion, has good weather resistance quick curing, stability, water resistance, toughness, resilience and good adhesion. |
| Solid content | 50±1wt% | |||
| Viscosity.cps(25℃) | 500-1500 | |||
| PH | 2.0-5.0 | |||
| Minimum Film Formation Temperature（MFT） | 0℃ | |||
| Ca2+ stability 5%CaCl2: emulsion =1:3, 48h, No Flocculation, No Stratification. | pass | |||
Waterborne polymer series for textile
| Product name | Performance indicators | applications | performance | |
| HN-5001 | Appearance | White milky liquid with yellow light | Textile screen printing paste | Soft, low adhesion, fastness, good adhesion |
| Solid content | 50±1wt% | |||
| Viscosity.cps(25℃) | 300-1000 | |||
| PH | 7.0-8.0 | |||
| Minimum Film Formation Temperature（MFT） | 0℃ | |||
| Ca2+ stability 5%CaCl2: emulsion =1:3, 48h, No Flocculation, No Stratification. | Pass | |||
| Product name | Performance indicators | applications | performance | |
| HN-9132 | Appearance | milk white liquid | Ink-jet printing coating adhesive | Nonionic emulsion, it can be used for printing layers based on non-woven fabric, cotton cloth and chemical fiber cloth. |
| Solid content | 53±1wt% | |||
| Viscosity.cps(25℃) | 500-2000 | |||
| PH | 3.0-4.0 | |||
| Glass Transition Temperature (Tg) | 5℃ | |||
| Minimum Film Formation Temperature（MFT） | 0-5℃ | |||
| Product name | Performance indicators | applications | performance | |
| HN-8321H | Appearance | light blue | Nylon and polyester fabric styling | Strong penetration, good fiber positioning effect, high stiffness |
| Solid content | 40±1wt% | |||
| Viscosity.cps(25℃) | 100-1000 | |||
| Particle Size（nm） | 120-140 | |||
| PH | 2.0-5.0 | |||
| Product name | Performance indicators | applications | performance | |
| HN-PW01 | Appearance | Milk white and light blue liquid | polyester wadding | Self-crosslinking type vinegar c adhesive, with strong mechanical stability and thermal stability, in soft water can be infinite dilution. Strong adhesion, easy to form film. Can be bonded with a variety of fibers, bonding strength, heat resistance, good fire resistance can be customized according to customer demand. |
| Solid content | 32±1wt% | |||
| Viscosity.cps(25℃) | ＜10 | |||
| PH | 3-5 | |||
| Glass Transition Temperature (Tg) | 19℃ | |||
| Product name | Performance indicators | applications | performance | |
| HN-CA01 | Appearance | Milk white and light blue liquid | Carpet gum | Moderate hardness, thermoplastic stability, good pile binding |
| Solid content | 30±1wt% | |||
| Viscosity.cps(25℃) | ＜10 | |||
| PH | 3-5 | |||
| Glass Transition Temperature (Tg) | 35℃ | |||
| HN-CA02 | Appearance | Milk white and light blue liquid | Carpet gum（foam adhesive） | Moderate hardness, thermoplastic stability, good pile binding |
| Solid content | 30±1wt% | |||
| Viscosity.cps(25℃) | ＜10 | |||
| PH | 3-5 | |||
| Glass Transition Temperature (Tg) | 31℃ | |||
Waterborne polymer series for building waterproofing coatings
| Product name | Performance indicators | applications | performance | |
| HN-351T | Appearance | light blue | Transparent waterproof adhesive | Good transparency, good weather resistance, good adhesion with substrate, excellent water resistance |
| Solid content | 38±1wt% | |||
| Viscosity.cps(25℃) | 100-2000 | |||
| PH | 7.0-8.0 | |||
| Product name | Performance indicators | applications | performance | |
| HN-3178 | Appearance | Milky white with a hint of green | Polymer cement waterproof mortar and polymer cement waterproof paste | New generation of environmentally friendly styrene-acrylic emulsion, does not contain APEO. Excellent cement workability and water resistance, good balance between flexibility and strength, ammonia taste up to standard and better mechanical properties, to meet the requirements of the industry for high performance. |
| Solid content | 49±1wt% | |||
| Viscosity.cps(25℃) | 100-1000 | |||
| PH | 9.0-10.0 | |||
| Minimum Film Formation Temperature（MFT） | 0℃ | |||
| Product name | Performance indicators | applications | performance | |
| HN-3168 | Appearance | Milky white with a hint of blue | Steel structure metal roofing waterproof coating and heat reflective coating | Good compatibility with cement, give the substrate excellent bonding strength, excellent impermeability. |
| Solid content | 54 ± 1％ | |||
| Viscosity.cps(25℃) | 500-2000 | |||
| PH | 8.5-9.5 | |||
| Minimum Film Formation Temperature（MFT）（℃） | 0℃ | |||
| Product name | Performance indicators | applications | performance | |
| HN-340T | Appearance | milk white liquid | Single component waterproof, putty, gigging paint | Self-crosslinking emulsion, has excellent flexibility, high elasticity, good weather and aging resistance and good adhesion. |
| Solid content | 56±1wt% | |||
| Viscosity.cps(25℃) | 1000-3000 | |||
| PH | 7.0-8.0 | |||
| Minimum Film Formation Temperature（MFT） | 0℃ | |||
| Ca2+ stability 5%CaCl2: emulsion =1:3, 48h, No Flocculation, No Stratification. | Pass | |||
| Product name | Performance indicators | applications | performance | |
| HN-332T | Appearance | Milky white with a hint of green | Elastomeric waterproofing coating, JS waterproof coating, putty, etc | Excellent cement compatibility, excellent low temperature performance, extensibility and tensile strength, excellent water, alkali and weather resistance. |
| Solid content | 56±1wt% | |||
| Viscosity.cps(25℃) | 1000-3000 | |||
| PH | 7.0-8.0 | |||
| Minimum Film Formation Temperature（MFT） | 0℃ | |||
| Ca2+ stability 5%CaCl2: emulsion =1:3, 48h, No Flocculation, No Stratification. | Pass | |||
| Product name | Performance indicators | applications | performance | |
| HN-3198 | Appearance | Milky white with a hint of blue | Color acrylic elastic waterproof coating, polymer-modified emulsified asphalt and road bridge emulsified asphalt waterproof coating | Excellent flexibility, no plasticizer, long effective elasticity and waterproof effect, excellent packing capacity and excellent mechanical stability, easy formula design, excellent durability and water resistance, strong adhesion to the substrate. |
| Solid content | 50±1wt% | |||
| Viscosity.cps(25℃) | 1000-3000 | |||
| PH | 7.0-8.0 | |||
| Minimum Film Formation Temperature（MFT） | 0℃ | |||
Waterborne polymer series for metal paint
| Product name | Performance indicators | applications | performance | |
| HN-5119 | Appearance | light blue | Color plate coating | Self-crosslinking styrene-acrylic emulsion, has high hardness, good weather resistance, high powder and color resistance, excellent adhesion, water resistance, salt spray resistance and flash rust resistance. |
| Solid content | 48±1wt% | |||
| Viscosity.cps(25℃) | 4000-6000 | |||
| PH | 7.0-8.0 | |||
| Glass Transition Temperature (Tg) | 25℃ | |||
| Minimum Film Formation Temperature（MFT） | 20-22℃ | |||
| Product name | Performance indicators | applications | performance | |
| HN-1019 | Appearance | light blue | Used for General steel structure, casting paint | Self-crosslinking styrene-acrylic emulsion has small particle size, good water resistance, high gloss, good compatibility with anti-rust agent and anti-rust pigment, excellent adhesion to metal base material. |
| Solid content | 46±2% | |||
| Viscosity.cps(25℃) | 1000-3000 | |||
| PH | 7.0-8.0 | |||
| Glass Transition Temperature (Tg) | 28℃ | |||
| Minimum Film Formation Temperature（MFT） | 80℃ | |||
| HN-AC610 | Appearance | light blue | Used for Steel structure, iron lacquer | Self-crosslinking acrylic emulsion, has high hardness, good weather resistance, high powder and color resistance, excellent adhesion, water resistance, salt spray resistance and flash rust resistance. |
| Solid content | 47±1wt% | |||
| Viscosity.cps(25℃) | <200 | |||
| PH | 7.0-8.0 | |||
| Glass Transition Temperature (Tg) | 35℃ | |||
| Minimum Film Formation Temperature（MFT） | 40℃ | |||
| Product name | Performance indicators | applications | performance | |
| HN-02BF | Appearance | light blue | Used for the preservative zinc plating board | Good compatibility with hexavalent chromium, compact paint film, water resistance, weather resistance, high adhesion, strong impact resistance. |
| Solid content | 37±1wt% | |||
| Viscosity.cps(25℃) | ≤500cps | |||
| PH | 2.0-4.0 | |||
| Ca2+ stability 15%CaCl2: emulsion =1:3, 48h, No Flocculation, No Stratification. | Pass | |||
| HN-5518 | Appearance | light blue | Used for the preservative zinc plating board | Good compatibility with hexavalent chromium, compact paint film, water resistance, weather resistance, high adhesion, strong impact resistance. |
| Solid content | 37±1wt% | |||
| Viscosity.cps(25℃) | ≤500cps | |||
| PH | 2.0-4.0 | |||
| Ca2+ stability 15%CaCl2: emulsion =1:3, 48h, No Flocculation, No Stratification. | Pass | |||
Waterborne polymer series for Printing ink
| Product name | Performance indicators | applications | performance | |
| HN-501NK | Appearance | light blue | Waterborne ink used in flexographic printing of paper substrate | Good solubility, high gloss, film forming performance, compatibility with fast – drying agent, substrate adhesion. |
| Solid content | 47±1wt% | |||
| Viscosity.cps(25℃) | 100-500 | |||
| Particle Size（nm） | 80-100 | |||
| PH | 6.0-8.0 | |||
| Glass Transition Temperature (Tg) | 10℃ | |||
| Product name | Performance indicators | applications | performance | |
| HN-YS861 | Appearance | light blue | Wallpaper printing inks | Self-crosslinking acrylic emulsion, has high gloss, fast drying speed, good weather resistance, non-yellowing, non-sticky, anti-plasticizer precipitation, good color development for various organic and inorganic pigments, strong adhesion to paper board, anti-adhesion outstanding. |
| Solid content | 42±1wt% | |||
| Viscosity.cps(25℃) | 100-1000 | |||
| Particle Size（nm） | 100-130 | |||
| PH | 6.0-8.0 | |||
| Glass Transition Temperature (Tg) | 60℃ | |||
| HN-YS961 | Appearance | light blue | Wallpaper printing inks | Self-crosslinking acrylic emulsion, has high gloss, fast drying speed, good weather resistance, non-yellowing, non-sticky, anti-plasticizer precipitation, good color development for various organic and inorganic pigments, strong adhesion to paper board, anti-adhesion outstanding. |
| Solid content | 42±1wt% | |||
| Viscosity.cps(25℃) | 100-1000 | |||
| Particle Size（nm） | 100-130 | |||
| PH | 6.0-8.0 | |||
| Glass Transition Temperature (Tg) | 70℃ | |||
| Product name | Performance indicators | applications | performance | |
| HN-PC12 | Appearance | light blue | Weak solvent ink printing coating | Anionic emulsion, with high gloss and excellent ink-absorbency, is used for printing layers based on non-woven fabric, cotton cloth and chemical fiber fabric. |
| Solid content | 37±1wt% | |||
| Viscosity.cps(25℃) | 600-1500 | |||
| PH | 7.0-8.0 | |||
| Glass Transition Temperature (Tg) | 12℃ | |||
| Minimum Film Formation Temperature（MFT） | 10-15℃ | |||
| HN-PC46 | Appearance | Milk white and light blue liquid | Weak solvent ink printing coating | Anionic emulsion, with high gloss and excellent ink absorption, is used on the printing layer based on non-woven fabric, cotton cloth and chemical fiber fabric (best used in conjunction with GK-PC12). |
| Solid content | 37±1wt% | |||
| Viscosity.cps(25℃) | 600-1500 | |||
| PH | 7.0-8.0 | |||
| Glass Transition Temperature (Tg) | 46℃ | |||
| Minimum Film Formation Temperature（MFT） | 55℃ | |||
| Product name | Performance indicators | applications | performance | |
| HN-9132 | Appearance | milk white liquid | Ink-jet printing coating adhesive | Nonionic emulsion, it can be used for printing layers based on non-woven fabric, cotton cloth and chemical fiber cloth. |
| Solid content | 53±1wt% | |||
| Viscosity.cps(25℃) | 500-2000 | |||
| PH | 3.0-4.0 | |||
| Glass Transition Temperature (Tg) | 5℃ | |||
| Minimum Film Formation Temperature（MFT） | 0-5℃ | |||
Waterborne polymer series for Wood coatings
| Product name | Performance indicators | applications | performance | |
| HN-MQ601 | Appearance | light blue | Wood varnish, high hardness white paint | High hardness, anti – adhesion, good stain resistance, water resistance, thickener response |
| Solid content | 44±1wt% | |||
| Viscosity.cps(25℃) | 100-1000 | |||
| PH | 7.0-8.0 | |||
| Minimum Film Formation Temperature（MFT） | 15 | |||
| HN-MQ602 | Appearance | light blue | Wood varnish, color paint | Good chemical resistance, alcohol resistance to coffee, good moisture resistance, good flexibility, good thickener response |
| Solid content | 44±1wt% | |||
| Viscosity.cps(25℃) | 100-1000 | |||
| PH | 7.0-8.0 | |||
| Minimum Film Formation Temperature（MFT） | 13 | |||
| HN-MQ603 | Appearance | light blue | Wood varnish | Wood grain definition, alcohol resistance, coffee resistance, flexibility, thickener response is good |
| Solid content | 40±1wt% | |||
| Viscosity.cps(25℃) | <500 | |||
| PH | 7.0-8.0 | |||
| Minimum Film Formation Temperature（MFT） | 15 | |||
| HN-GR01 | Appearance | light blue | Light paint system stain resistant dispersion resin | To improve the stain resistance of light paint to coffee, seasoning and other colored liquids |
| Solid content | 50±1wt% | |||
| Viscosity.cps(25℃) | <500 | |||
| Particle Size（nm） | 40-60 | |||
| PH | 7.0-8.0 | |||
Soil and sand curing agent
Introduction: Soil curing agents are used for the hardening of soil roads. By spraying the curing agent, stirring the soil, and compacting with a road roller, a waterproof and hard road with a specific strength to walk and for vehicle passing is formed. It has the characteristics of simple, rapid, environmentally friendly, odorless, and low requirements for mechanical equipment.
Polymer emulsion properties affect the strength of the road, water resistance, wear resistance, and aging resistance.
| Product name | Performance indicators | applications | performance | |
| HN-152VA | Appearance | milk white liquid | Sand and dust curing agent | In the natural environment, the degradation rate is fast, pollution-free, suitable for frequent spraying work environment |
| Solid content | 50±1wt% | |||
| Viscosity.cps(25℃) | <500 | |||
| PH | 2.0-5.0 | |||
| Minimum Film Formation Temperature（MFT） | 0℃ | |||
| Ca2+ stability 5%CaCl2: emulsion =1:3, 48h, No Flocculation, No Stratification. | Pass | |||
| HN-158T | Appearance | light blue | Sand and dust curing agent | Silicone modified styrene-acrylic emulsion has high dilution ratio. Film strength and toughness, sand, dust adhesion relay strong, room temperature self-forming film, film weather resistance can be excellent, can ensure long-term effect. |
| Solid content | 50±1wt% | |||
| Viscosity.cps(25℃) | 1500-3000 | |||
| Particle Size（nm） | 90-160 | |||
| PH | 6.0-7.0 | |||
| Minimum Film Formation Temperature（MFT） | 0℃ | |||
| Ca2+ stability 5%CaCl2: emulsion =1:3, 48h, No Flocculation, No Stratification. | Pass | |||
Coating additives
| Product name | Performance indicators | applications | performance | |
| AT-01 | Appearance | Milk white and light blue liquid | Thickening agent for water-based coating | Added tocoating to improve some properties, such as flow, levelling and anti-hanging. |
| Solid content | 30±1wt% | |||
| Viscosity.cps(25℃) | ≤100cps | |||
| PH | 2.0-4.0 | |||
| ATW-60 | Appearance | Milk white and light blue liquid | This emulsion copolymer has good thickening effect and strong thixotropy. | |
| Solid content | 30±1wt% | |||
| Viscosity.cps(25℃) | ≤100cps | |||
| PH | 2.0-4.0 | |||
| ATW-80 | Appearance | Milk white and light blue liquid | This emulsion copolymer has good thickening effect and strong thixotropy. | |
| Solid content | 28±1wt% | |||
| Viscosity.cps(25℃) | ≤100cps | |||
| PH | 2.0-4.0 | |||
| ATW-2000 | Appearance | Milk white and light blue liquid | This thickening agent has better levelling property and can improve medium and high shear viscosity. | |
| Solid content | 25±1wt% | |||
| Viscosity.cps(25℃) | ≤30cps | |||
| PH | 3.0-4.0 | |||
| ATW-3000 | Appearance | Milk white and light blue liquid | Alkali solubilization thickener with excellent thickening effect and leveling property | |
| Solid content | 30±1wt% | |||
| Viscosity.cps(25℃) | ≤30cps | |||
| PH | 3.0-4.0 | |||
| WP-19 | Appearance | Light yellow | Dispersing agent for water-based coating | The dispersant has good dispersing effect on inorganic pigments and good stability of coatings. |
| Solid content | 40±1wt% | |||
| Viscosity.cps(25℃) | ≤500 cps | |||
| PH | 7.5-9.0 | |||
| WP-5040 | Appearance | Light yellow | The dispersant can significantly improve the leveling property and anti-sinking property of the coating, and can be used as a part of the film forming material into the coating. | |
| Solid content | 40±1wt% | |||
| Viscosity.cps(25℃) | ≤500 cps | |||
| PH | 7.5-9.0 | |||